The aim of this in vitro study was to evaluate the effect of air polishing on the implant abutment surface using different abrasive powders: sodium bicarbonate and amino acid glycine. Fifteen grade III machined surface titanium disks with 8-mm diameter and 2-mm thickness were divided in 3 groups of 5 samples each and subjected to air polishing for 20 seconds with an Ultrajet Flex air-abrasive device and a distinct prophylaxis protocol: air and water (G1); air, water, and sodium bicarbonate (G2); and air, water; and amino acid glycine (G3). After the air polishing, the average roughness (Ra) of the samples was measured using an optical profilometer, and the obtained data were statistically analyzed. We found that G1 and G3 had similar Ra, while Ra values for G2 were significantly higher. This study demonstrated that air-polishing powders containing glycine had less of an effect on the roughness of the surface of titanium disks compared with sodium bicarbonate powders. Future in vivo studies will be conducted to investigate the clinical relevance of the present results.

Evaluation of the Effect of Air Polishing With Different Abrasive Powders on the Roughness of Implant Abutment Surface: An In Vitro Study

Perrotti, Vittoria
Co-primo
;
D'Arcangelo, Camillo;Tumedei, Margherita;
2019-01-01

Abstract

The aim of this in vitro study was to evaluate the effect of air polishing on the implant abutment surface using different abrasive powders: sodium bicarbonate and amino acid glycine. Fifteen grade III machined surface titanium disks with 8-mm diameter and 2-mm thickness were divided in 3 groups of 5 samples each and subjected to air polishing for 20 seconds with an Ultrajet Flex air-abrasive device and a distinct prophylaxis protocol: air and water (G1); air, water, and sodium bicarbonate (G2); and air, water; and amino acid glycine (G3). After the air polishing, the average roughness (Ra) of the samples was measured using an optical profilometer, and the obtained data were statistically analyzed. We found that G1 and G3 had similar Ra, while Ra values for G2 were significantly higher. This study demonstrated that air-polishing powders containing glycine had less of an effect on the roughness of the surface of titanium disks compared with sodium bicarbonate powders. Future in vivo studies will be conducted to investigate the clinical relevance of the present results.
File in questo prodotto:
File Dimensione Formato  
2019 Biazussi et al. JOI.pdf

Solo gestori archivio

Descrizione: Research Article
Tipologia: PDF editoriale
Dimensione 163.25 kB
Formato Adobe PDF
163.25 kB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11564/705945
Citazioni
  • ???jsp.display-item.citation.pmc??? 2
  • Scopus 6
  • ???jsp.display-item.citation.isi??? 7
social impact