The prototype of an amperometric glucose biosensor was realized by thermal inkjet printing using biological and electronic water-based inks, containing a glucose oxidase (GOD) from Aspergillus niger and the conducting polymer blend poly(3,4-ethylenedioxythiophene/polystyrene sulfonic acid) (PEDOT/PSS), respectively. The biosensor was fabricated microdepositing PEDOT/PSS and GOD, in sequence, on ITO-glass, by a commercial inkjet printer, with the help of a commercial software. High density microdots matrices were so-realized, with a calculated resolution of about 221 × 221 dpi (dot per inch). By means of a rapid and easy assay it was demonstrated that no activity loss occurred upon the printing of GOD, despite of the use of a thermal printhead. The device was encapsulated in a semipermeable membrane of cellulose acetate, applied by dip-coating, in order to prevent dissolution of the enzyme and/or PEDOT/PSS in water. The preliminary response of the electrode was measured in an aqueous glucose solution in the presence of ferrocenemethanol (FeMeOH) as a mediator, and resulted linear up to 60 mM in glucose. The best sensitivity value achieved was 6.43 μA M-1 cm-2 (447 nA M-1 U -1 cm-2). The characteristics of the device, and the possible performance improvements have been analyzed and discussed. The reported findings indicate that inkjet printing could be a viable instrument for the easy construction of a working biosensor via direct digital design using biological and conductive polymer based inks. Such an approach may be seen as an example of "biopolytronics". © 2004 Elsevier B.V. All rights reserved.
An amperometric glucose biosensor prototype fabricated by thermal inkjet printing
FRALEONI MORGERA, Alessandro;
2005-01-01
Abstract
The prototype of an amperometric glucose biosensor was realized by thermal inkjet printing using biological and electronic water-based inks, containing a glucose oxidase (GOD) from Aspergillus niger and the conducting polymer blend poly(3,4-ethylenedioxythiophene/polystyrene sulfonic acid) (PEDOT/PSS), respectively. The biosensor was fabricated microdepositing PEDOT/PSS and GOD, in sequence, on ITO-glass, by a commercial inkjet printer, with the help of a commercial software. High density microdots matrices were so-realized, with a calculated resolution of about 221 × 221 dpi (dot per inch). By means of a rapid and easy assay it was demonstrated that no activity loss occurred upon the printing of GOD, despite of the use of a thermal printhead. The device was encapsulated in a semipermeable membrane of cellulose acetate, applied by dip-coating, in order to prevent dissolution of the enzyme and/or PEDOT/PSS in water. The preliminary response of the electrode was measured in an aqueous glucose solution in the presence of ferrocenemethanol (FeMeOH) as a mediator, and resulted linear up to 60 mM in glucose. The best sensitivity value achieved was 6.43 μA M-1 cm-2 (447 nA M-1 U -1 cm-2). The characteristics of the device, and the possible performance improvements have been analyzed and discussed. The reported findings indicate that inkjet printing could be a viable instrument for the easy construction of a working biosensor via direct digital design using biological and conductive polymer based inks. Such an approach may be seen as an example of "biopolytronics". © 2004 Elsevier B.V. All rights reserved.File | Dimensione | Formato | |
---|---|---|---|
1-s2.0-S0956566304004208-main.pdf
Solo gestori archivio
Descrizione: Article
Tipologia:
PDF editoriale
Dimensione
329.15 kB
Formato
Adobe PDF
|
329.15 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.