Mechanical Properties of Translucent Zirconia: An In Vitro Study

Background: The introduction of translucent zirconia has improved mimetics: nevertheless, a reduction in the mechanical performance was registered. The study aim was to investigate the mechanical characteristics of a high-translucent zirconia used for monolithic restorations before and after the aging process compared to a low-translucent zirconia. Methods: A total of 23 specimens were used in the present study. Group A (n = 10) was made of a high-translucent Y-TZP; group B (n = 7) was made of a low-translucent Y-TZP and finally group C (n = 6) was an aged high-translucent Y-TZP. Flexural strength, fracture toughness, brittleness, microcrack’s propagation and grain size were analyzed. Results: The Vickers hardness was: 1483 ± 187 MPa (group C); 1102 ± 392 MPa (group A); 1284 ± 32 MPa (group B). The flexural strength was: 440 (±96.2) MPa (group C); 427 (±59.5) MPa (group A); 805 (±198.4) MPa (group B). The fracture toughness was: 5.1 (±0.7) MPa.m1/2 (group C); 4.9 (±0.9) MPa.m1/2 (group A); 8.9 (±1.1) MPa.m1/2 (group B). The brittleness was: 295 (±42.8) (group C), 230.9 (±46.4) (group A) and 144.9 (±20.3) (group B). The grain size was: 2.75 (±1.2) µm2 (group A); 0.16 (±0.05) µm2 (group B); 3.04 (±1.1) µm2 (group C). Conclusions: The significant reduction in the mechanical properties of high-translucent zirconia, compared to the traditional one, suggests their use in the anterior/lateral area (up to premolars).