Background/Objectives: The aim of this in vitro study was to analyze and compare the Streptococcus mutans ability to adhere and form biofilm on the surface of light-cured VS heat-cured dental composite resins; Methods: Three composite resins with different chemical formulations were selected: GrandioSO (GR), Venus Diamond (VD) and Enamel Plus Hri Biofunction (BF). Disk-shaped specimens were manufactured by light-curing the composite resins (light-cured subgroups) and subjecting them to a further heat-curing cycle at 80° for 10 min (heat-cured subgroups). Specimens were analyzed for planktonic CFU count (CFU/mL), sessile CFU count (CFU/mL) and for biomass quantification (OD570nm); Results: The planktonic CFU count was higher in all the light-cured subgroups than in the heat-cured subgroups (light-cured: GR = 7.23 × 106, VD = 2.14 × 107, BF = 4.40 × 107; heat-cured: GR = 4.89 × 106, VD = 4.95 × 106, BF = 2.80 × 107), with a statistically significant increase for BF and VD. Focusing on the sessile CFUs, both GR (light-cured = 7.49 × 106; heat-cured = 3.97 × 106) and VD (light-cured = 2.93 × 107; heat-cured = 6.07 × 106) showed a significantly increased number of colonies in the light-cured subgroups. The OD570nm values recorded for the light-cured BF subgroup (0.4280) were significantly increased compared to the heat-cured BF subgroup (0.1931); Conclusions: A more complete polymerization protocol seems to lead to a potential reduction in the risk of secondary caries.

Influence of Polymerization Protocol on Adhesion and Proliferation of Streptococcus mutans on Three Dental Composite Resins

Francesco De Angelis
;
Camillo D’Arcangelo;Silvia Di Lodovico;Edoardo Sorrentino;Matteo Buonvivere;Simonetta D’Ercole
2024-01-01

Abstract

Background/Objectives: The aim of this in vitro study was to analyze and compare the Streptococcus mutans ability to adhere and form biofilm on the surface of light-cured VS heat-cured dental composite resins; Methods: Three composite resins with different chemical formulations were selected: GrandioSO (GR), Venus Diamond (VD) and Enamel Plus Hri Biofunction (BF). Disk-shaped specimens were manufactured by light-curing the composite resins (light-cured subgroups) and subjecting them to a further heat-curing cycle at 80° for 10 min (heat-cured subgroups). Specimens were analyzed for planktonic CFU count (CFU/mL), sessile CFU count (CFU/mL) and for biomass quantification (OD570nm); Results: The planktonic CFU count was higher in all the light-cured subgroups than in the heat-cured subgroups (light-cured: GR = 7.23 × 106, VD = 2.14 × 107, BF = 4.40 × 107; heat-cured: GR = 4.89 × 106, VD = 4.95 × 106, BF = 2.80 × 107), with a statistically significant increase for BF and VD. Focusing on the sessile CFUs, both GR (light-cured = 7.49 × 106; heat-cured = 3.97 × 106) and VD (light-cured = 2.93 × 107; heat-cured = 6.07 × 106) showed a significantly increased number of colonies in the light-cured subgroups. The OD570nm values recorded for the light-cured BF subgroup (0.4280) were significantly increased compared to the heat-cured BF subgroup (0.1931); Conclusions: A more complete polymerization protocol seems to lead to a potential reduction in the risk of secondary caries.
2024
Inglese
ELETTRONICO
12
10
14
Article number: 2235
Streptococcus mutans; composite resins; light-cured; heat-cured; polymerization
https://www.mdpi.com/2227-9059/12/10/2235
no
6
info:eu-repo/semantics/article
262
DE ANGELIS, Francesco; D’Arcangelo, Camillo; DI LODOVICO, Silvia; Sorrentino, Edoardo; Buonvivere, Matteo; D’Ercole, Simonetta
1 Contributo su Rivista::1.1 Articolo in rivista
open
File in questo prodotto:
File Dimensione Formato  
2024 De Angelis D_Ercole biomedicines-.pdf

accesso aperto

Tipologia: PDF editoriale
Dimensione 8.16 MB
Formato Adobe PDF
8.16 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11564/841611
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact